Qian, PingpingTang, ZhenghuaWang, LiSiyasiya, Charles Witness2020-11-182020-11-182020-03-25Qian, P.P., Tang, Z.H., Wang, L. et al. 2020, 'Hot deformation characteristics and 3-D processing map of a high-titanium Nb-micro-alloyed steel', Materials, vol. 13, art. 1501, pp. 1-16.1996-1944 (online)10.3390/ma13071501http://hdl.handle.net/2263/77066Hot deformation behavior of a high-titanium Nb-micro-alloyed steel was investigated by conducting hot compression tests at the temperature of 900–1100 °C and the strain rate of 0.005–10 s−1. Using a sinh type constitutive equation, the apparent activation energy of the examined steel was 373.16 kJ/mol and the stress exponent was 6.059. The relations between Zener–Hollomon parameters versus peak stress (strain) or steady-state stress (strain) were successfully established via the Avrami equation. The dynamic recrystallization kinetics model of the examined steel was constructed and the validity was confirmed based on the experimental results. The 3-D atomic distribution maps illustrated that strain can significantly affect the values of power dissipation efficiency and the area of instability domains. The 3-D processing maps based on a dynamic material model at the strains of 0.2, 0.4, 0.6 and 0.8 were established. Based on traditional and 3-D processing maps and microstructural evaluation, the optimum parameter of for a high-titanium Nb-micro-alloyed steel was determined to be 1000–1050 °C/0.1–1 s−1.en© 2020 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution (CC BY) license.High-titanium Nb-micro-alloyed steelDeformation behaviorConstitutive modellingTraditional and 3-D processing mapsEngineering, built environment and information technology articles SDG-07SDG-07: Affordable and clean energyEngineering, built environment and information technology articles SDG-09SDG-09: Industry, innovation and infrastructureEngineering, built environment and information technology articles SDG-12SDG-12: Responsible consumption and productionEngineering, built environment and information technology articles SDG-13SDG-13: Climate actionArticle