Low temperature vaporisation of Cr from fluoride flux reacted at 1350 ° C with Al -Cr -Fe powder : thermochemical analysis of gas phase reactions and nano-strand formation
JavaScript is disabled for your browser. Some features of this site may not work without it.
Please be advised that the site will be down for maintenance on Sunday, September 1, 2024, from 08:00 to 18:00, and again on Monday, September 2, 2024, from 08:00 to 09:00. We apologize for any inconvenience this may cause.
Low temperature vaporisation of Cr from fluoride flux reacted at 1350 ° C with Al -Cr -Fe powder : thermochemical analysis of gas phase reactions and nano-strand formation
The submerged arc welding (SAW) process is complex because multi-phase reactions occur simultaneously across a large temperature interval from 2500 °C in the arc cavity, down to the weld pool liquidus temperare at the slag-weld pool interface. This complexity hinders research on specific process metallurgy aspects, such as gas formation from the oxy-fluoride slag. The main objective of this work is to illustrate a low temperature experimental technique as an accurate reaction simulation experiment of SAW flux oxy-fluoride slag behaviour in terms of gas formation and metal powder assimilation reaction mechanisms as observed in the SAW process. The oxy-fluoride slag behaviour was confirmed by identification and analyses of nano-strand formation in the reacted slag formed from the reaction of welding flux with Al-Fe-Cr metal powders at 1350 °C. The observed nano-strand formation agrees with similar observations in SAW post-weld slags used to confirm of oxy-fluoride vaporisation and re-condensation. Element distribution from energy dispersive X-ray spectroscopy (EDS) maps and thermochemical calculations were used to gain insights into the reactions in nano-strand formation. The nano-strands contained chromium patches and spots of less than 1 μm in scale, confirming that added Cr metal powder assimilated via the gas phase. Cr-fluoride formed part of the oxy-fluoride slag and likely formed Cr-fluoride gas. Cr was recovered via re-condensation of Cr vapour formed from the reaction of Cr-fluoride with Al gas. This work presents an accurate low temperature simulation method of gas formation and metal powder assimilation reactions in oxy-fluoride slags as in the SAW process.