Cold-pressing and vacuum arc melting of γ-TiAl based alloys
Mathabathe, Maria Ntsoaki; Bolokang, A.S.; Govender, G.; Siyasiya, Charles Witness; Mostert, Roelf Johannes
Beta (β) solidifying γ-TiAl intermetallic alloys of nominal composition Ti-48Al, Ti-48Al-2Nb, Ti-48Al-2Nb-0.7Cr alloys have been cold pressed and vacuum arc melted. The Al loss was due to compaction method used prior to the melting technique, since it was evident after compaction that Al particles migrated to the surface in contact with the die facets after cold pressing. Electron backscatter diffraction (EBSD)-orientation mapping demonstrated that the α-precipitation from the parent β-phase follows the Blackburn orientation relationship (BOR). Microstructural characterization of the alloys was studied by scanning electron microscopy (SEM) equipped with energy dispersion spectroscopy (EDS) for micro-analysis. X-ray diffraction (XRD) technique was used to detect phase compositions.
Tang, Zhenghua(University of Pretoria, 2007-08-01)
Thinner walled (about 6 mm thickness) line pipe steels for smaller diameter pipelines tend to have a relatively high ratio of yield strength to ultimate tensile strength (YS/UTS) of 0.93 or higher. This study focused on ...
Among many shape memory alloys, Ti-Pt alloys have potential as a high temperature shape memory alloy. The alloy undergoes a reversible martensitic transformation at temperatures above 1000 oC. However, the alloy’s negligible ...
Semi-solid metal high pressure die casting was used to produce plates from traditional wrought Al-Mg-Si alloys 6082 and 6004, as well as from traditional casting Al-Si-Mg alloys A356 and F357. The high Si-content of the ...