High electrochemical performance of hierarchical porous activated carbon derived from lightweight cork (Quercus suber)

Abstract

Activated carbon (AC) derived from biomass lightweight cork (Quercus suber) material was synthesized by KOH activation with different mass ratios of Q. suber: KOH in order to investigate the electrochemical properties of the AC in relation to KOH concentration. A well-defined porous activated carbon was obtained with a high surface area of 1081 m2 g−1 and a high pore volume of 0.66 cm3 g−1 when the Q. suber: KOH mass ratio was fixed at 1:2. A specific capacitance of 166 F g−1 was obtained for the symmetric device at 0.5 A g−1 in 1 M Na2SO4 with energy and power densities of 18.6 and 449.4 W Kg−1, respectively. The device displays good cycling stability after floating test for 200 h at 1.8 V and also displays 99.8% capacitance retention after cycling for 5000 cycles. The excellent electrochemical performance of the device makes it a potential material for supercapacitor application.