Abstract:
A one-step solvothermal approach was used to integrate nitrogen-doped reduced graphene oxide into
vanadium dioxide (VO2) to prepare a V@XN-G (where X = 24, 48 and 96 and is the mass of urea as the
nitrogen (N) source) nanocomposite material. After optimization, V@48N-G showed better performance
with a specific capacitance of 197.4 F g 1 at 0.5 A g 1 in a wide working potential window of 0.0–0.8 V vs.
silver/silver chloride and was adopted as a positive electrode. Thus, cocoa waste-based activated carbon
(ACC) was investigated and considered a negative electrode in assembling an asymmetric full-cell V@48NG//
ACC. The device exhibited good specific energy and power of 28.8 W h kg 1 and 425.1 W kg 1,
respectively, at a voltage window and specific current of 1.7 V and 0.5 A g 1, respectively. Its cycling stability
resulted in a Coulombic efficiency (CE) and capacitance retention (CR) of 99.8% and 73%, respectively, over
10000 galvanostatic charge/discharge cycles at 10 A g 1. Therefore, the V@48N-G//ACC device shows
excellent electrochemical performance and is suitable for energy storage application technology.